ASME SA537 Class 2 Carbon Steel Plates, ASTM A537 CL. 2

The a537 Class 2 Plate is heat treated using tempered and quenched methods and other material used for manufacturing these plates has yield strength, higher tensile strength, and corrosion resistance. The raw material is well tested and inspected and used according to the international quality standard. ASTM A537 CL1 Steel - Low Carbon Steel - MatmatchDescription TJC Steel can supply A537 Class 1/ A537 Cl1 pressure vessel steel plate, mainly used in construction for pressure vessels. This material data has been provided by TJC Iron & Steel. All metrics apply to room temperature unless otherwise stated.

ASTM A537 Class 1 Carbon Steel Plates SA537 CL. 1

The ASTM A537 Class 1 Pressure Vessel Plates range in length from 6m, 12m and to cut lengths.Customized lengths are also produced. The finish of the material can be natural or painted. The Hot Rolled Steel ASME SA537 Class 1 Plates are high strength plates that are heat treated.These are applied in pressure vessels. Boilers, heat exchangers, super heaters, chemical tankers, storage Steel Plate ASTM A537/A537M Class 3 Class 2 Class 1 in Steel Plate ASTM A537/A537M Class 3 Class 2 Class 1 in Large Stocl for Sale with Best Price and Quality. ASTM A537 Class 3(A537CL3) MATERIAL C Mn Si P S ASTM A537 Class 3(A537CL3) 0.24 0.13-0.55 0.92-1.72 0.035 0.035 MATERIAL Tensile Strength(MPa) Y Table 1 Material Specification List:Applicable ASTM GROUP 1 MATERIALS Material Forgings Castings Plates Bars Tubular Group Nominal Spec. Spec. Spec. Spec. Spec. No. Designation No. Grade No. Grade No. Grade No. Grade No. Grade 1.1 CSi A 105 A 216 WCB A 515 70 A 105 CMnSi A 350 LF2 A 516 70 A 350 LF2 A 672 C 70 A 537 Cl. 1 A 696 C A 672 B 70 31 2Ni A 350 LF3 A 350 LF3

using material sa-537 cl1 or cl2 - Metal and Metallurgy

May 12, 2016 · The Class 2 has higher values. RE:using material sa-537 cl1 or cl2. pradipgoswami (Materials) 13 May 16 02:07. Both are C-Mn (1.4% max) steels. Class 1 is Normalized-70 Ksi UTS category, while Cl2 is Q&T grade with nominal UTS-80 Ksi. For the above design temperature both grades would be appropriate, with reasonably good impact values @- (-)10 ASTM A537 / A537M - 20 Standard Specification for Pressure The steel shall be killed and undergo normalization, quenching and tempering. Heat and product analyses shall be performed on the materials and results shall conform to the required values in chemical composition in carbon, manganese, phosphorus, sulfur, silicon, copper, nickel, chromium and